ER 5183 aluminum TIG welding rod for boiler/ship building
ER5183 is a magnesium close to 5% and higher manganese content of aluminum magnesium welding Rod, with good corrosion resistance, heat resistance, high strength, good ductility. After the welding of the welding seam is still white, it can provide a good color for the welded joints. For some of the alloys, the strength of the welded joints is slightly higher than 5356.
Application of 5183 aluminum welding rod
the 5183 aluminum welding rod is used as a filler metal for argon arc welding of aluminum magnesium (3%Mg) alloy, which is used in the locomotive, chemical pressure vessel, nuclear industry, shipbuilding, refrigeration, boiler and aerospace industry.

Physical Property
Density (kg/dm3)	Melting temperatureºC	Thermal conductivity w/m•K	Linear expansion coefficient 10¯6/K(20-100ºC)	Electric conductivity % IACS
2.65	574-638	120	24.2	29

Weld Mechanical Properties (reference value)
Tension Strength(MPa)	Yield Strength(MPa)	Elongation (%)
275--300	125--140	15--20

ER5183 Aluminium & Aluminium Alloy welding Rods
Classification	GB/T 10858-2008 AWS A5.10···· ER 5183
Typical composition in %	Si··················· <0.40Fe··················· <0.40Cu··················· <0.10Mn················· 0.05-1.00Mg················· 4.30-5.20Cr················· 0.05-0.25Zn·················· <0.25Be·················· <0.0003Ti·················· <0.15Others·············· <0.05Others Total········· <0.15
Physical properties(Approx.Values)	0.2% yield strength Rpo2 (Mpa)···· 125 Tensile Strength Rm (Mpa)····· 275Elongation A5 (L0=5d0) (%)······ 17Test Temperature (ºC)······ 20
Performance & Usage	This type of product is widely used in general welding material with the Mg of 4.5%, which can be used in jointing or overlay forging and casting alloys processing in the same grade. Usage:pressure vessel,nuclear,ship-building,boiler,space industry ,etc .
Shielding gas	Argon, Helium, or Argon/Helium-mixtures.
Dimensions Φ	MIG - Rods (mm):0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4TIG - rods(mm):1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
Rod Packagings	Mig Rods:S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
	Tig Rod :5/10kg ······· length :1000mm