Jun 13, 2023
Diagnosing porosity issues in vertical
Funtay / iStock / Getty Images Plus Our shop recently added gas metal arc welding-pulse (GMAW-P) capabilities using solid wire and a 92% argon/8% CO2 gas blend. Historically, we have used CO2
Funtay / iStock / Getty Images Plus
Our shop recently added gas metal arc welding-pulse (GMAW-P) capabilities using solid wire and a 92% argon/8% CO2 gas blend. Historically, we have used CO2 gas-shielded flux-cored products for all our carbon steel manual welding, but deposition efficiency improvements and fume level reduction prompted the change. The welders struggle with porosity issues when using GMAW-P in vertical-up welds. This happens typically in deeper groove welds where access to the root can sometimes be a challenge. Any ideas?
To start, let's define what welding porosity is.
Porosity occurs when nitrogen, hydrogen, or oxygen become trapped in the solidifying weld metal as small gas bubbles. The sources of these three elements are atmospheric air, moisture, or the burning of hydrocarbons such as grease and oil. The welding arc is extremely hot, which causes these molecules to separate into their respective elements: hydrogen, nitrogen, carbon, and/or oxygen. These elements can reach levels beyond what filler metal deoxidizers can remove from the molten weld puddle and become trapped, resulting in porosity.
We are missing a little bit of information such as welding parameters, wire diameter and type, and any details about the base material. Occasionally, something minor in the details will jump out as the cause.
To minimize the potential for porosity, follow these basic good welding practices:
With the information you provided, let's examine what may be causing the porosity. Assuming the weld joint is clean and you follow good welding practices, then it may be something a little more subtle.
Gas-shielded flux-cored wires are resilient when dealing with less-than-perfect weld conditions. The weld protection they provide with the slag layer and external shielding gas make them very robust for many applications. Because of these features, your welders most likely experience few issues with them.
Comparatively, solid wires do not offer the same benefits. They lack the slag layer, which can provide additional weld metal protection when you lose shielding gas or the additional deoxidizers. Additionally, CO2 shielding gas provides great cleaning action on contaminants such as rust and mill scale. The solid-wire shielding gas you're using contains mostly argon—which is nonreactive—and a small amount of CO2 compared to the flux-cored wire, which reduces the cleaning action.
You stated the main porosity areas are hard-to-reach, vertical-up groove weld joints. This brings proper shielding gas coverage into consideration. If the joints are difficult to reach, it is possible your ESO is excessive, which can lead to a lack of shielding gas protection. If you are using standard 5/8-in. weld gun nozzles, this will force the welder to use an excessive ESO to see and access the joint.
However, if you are using 3/8-in. tapered gas nozzles, you will want to verify shielding gas flow rate at the nozzle.
The general recommendation for non-helium shielding gas flow rates is 25 to 35 cubic feet per hour (CFH) for small-diameter wires and 35 to 45 CFH for large-diameter wires with standard nozzles. If you are using the 3/8-in. tapered nozzles, you will want to set the flow rate no higher than 30 CFH. The reason is for a set volume of gas to exit the nozzle, it will have an associated velocity. As you increase flow rate, the velocity increases as well. When you increase flow rates above 45 CFH in standard nozzles, the exiting gas velocity creates a vacuum near the end of the nozzle opening, which may aspirate atmospheric air into the shielding gas plume. The exiting shielding gas velocity in tapered nozzles may become excessive at much lower flow rates, which can produce the same issues. Not only can this produce porosity, it is simply a waste of shielding gas.